| 牌號 Grade | 剩磁 Br | 矯頑力 Hcb | 內稟矯頑力 Hcj | 最大磁能職 (BH)max | 材料 Materlial | 應用 Application |
|---|---|---|---|---|---|---|
| 等方性胶磁 | 175-195mT | 125-140Ka/M | 150-175kA/m | 4.5-4.6kJ/m | Ba0.6FoxO | 微電機 Micro-motor |
| ALR-1A | 1750-1950 Gs | 1508-1760 Oe | 1886-2200 Oe | 0.56-0.58 MGOe | 混合CPE | 吸利器 Holder |
| 異方性胶磁 | 225-255 mT | 159.2-183 Ka/M | 179.1-202.9 kA/m | 10.4-12.0 kJ/m | Sr0.6Fo₂O | |
| ALR-2C | 2250-2550 Gs | 2000-2300 Oe | 2060-2480 Oe | 1.3-1.5 MGOe | 混合CPE | |
| 異方性胶磁 | 240-270 mT | 167.2-191 Ka/M | > 199 kA/m | 11.2-12.8k KJ/m | Sr0.6Fo₂O | |
| ALR-2E | 2400-2700 Gs | 2100-2400 Oe | >2550 Oe | 1.4-1.6 MGOe | 混合CPE | |
| 異方性胶磁 | 230-270 mT | 167-199 Ka/M | 210.7-266.7kA/m | 12.0-13.8 kJ/m | Sr0.6FoO | 微電機 |
| ALR-3A | 2300-2700 Gs | 2100-2400 Oe | 2650-2350 Oe | 1.5-1.7 MGOe | 混合NBR | Micro-motor |
| 異方性胶磁 | 230-260 mT | 163-195 Ka/M | 237-283 kA/m | 11.2-12.8 kJ/m | Sr0.6FoO | 家用電器 |
| ALR-3B | 2300-2600 GS | 2050-2450 Oe | 2950-2650 Oe | 1.4-1.6 MGOe | 混合NBR | House Hold Applance |
| 異方性胶磁 | 225-255 mT | 171-203 Ka/M | 258.4-314.4 kA/m | 11.2-12.8 kJ/m | Sr0.6FoO | 辦公自動化設備 |
| ALR-3C | 2250-2550 Gs | 2150-2550 Oe | >3260-3950 Oe | 1.4-1.6 MGOe | 混合NBR | OA Facilities |
| 牌號Grade | 密度Density | 肖氏硬度Hardness | 溫度系數Relative Temperature | 使用溫度Operation Temperature | 彈性Elasticity | 生產方式Production Fashion |
|---|---|---|---|---|---|---|
| 單位 Unit | g/cm | 8HORED | %/C | C | Kgf/mm2 | 擠出壓延法 |
| ALR-1A | 3.6-3.7 | 30-45 | -0.2 | -120 良好 | 壓延法 | |
| ALR-2C | 3.6-3.7 | 30-60 | -0.2 | -120 良好 | 壓延法 | |
| ALR-2E | 3.6-3.7 | 30-60 | -0.2 | -120 良好 | 壓延法 | |
| ALR-3A | 3.6-3.8 | 30-45 | -0.18 | -140 良好 | 壓延法 | |
| ALR-3B | 3.6-3.8 | 30-45 | -0.18 | -140 良好 | 壓延法 | |
| ALR-3C | 3.6-3.8 | 30-45 | -0.18 | -140 良好 | 壓延法 |